Semiconductor wafer, semiconductor chip and dicing method of a semiconductor wafer

ABSTRACT

The metal wirings of the uppermost layer are exposed so as to be contactable to the probe and arranged so as to be spatially separated from one another via spaces that are approximately parallel to the longitudinal direction of the dicing area, and the position and size of the space is designed considering a thickness of a cutting edge of a blade and relative positioning error, and the blade does not cross any metal wirings when the blade passes through the dicing area, thereby preventing the generation of an abruption or a burr due to the dicing to enhance a yield in IC production.

BACKGROUND OF THE INVENTION

1. Field of the Invention

The present invention relates to a semiconductor wafer having a characteristic evaluating device and a monitoring pad formed in a dicing area and a semiconductor chip obtained by cutting this wafer. Further, the present invention relates to a dicing method for cutting such a wafer.

2. Description of the Background Art

FIGS. 11A-11C are explanatory views showing one example of a conventional process for producing an IC (Integrated Circuit), wherein FIG. 11A shows a dicing process, FIG. 11B shows a state after dicing and FIG. 11C shows a wire bonding process. A wafer 1 is composed of a substrate 2 comprising a semiconductor of Si or GaAs and an electrical insulating layer 3 and/or metal wiring 4 formed on the substrate 2. Generally, chip areas where a large number of semiconductor devices are integrated are arranged in a matrix.

When an individual chip is taken out from the wafer 1, a blade 9 passes between each chip area for cutting each chip area as shown in FIG. 11A. When the metal wiring 4 exists on a passage line of the blade 9, a dicing stress is applied to the metal wiring 4 to cause a partial separation of the metal wiring 4 in the case of weak adhesion to a underlayer, with the result that a burr 4 a is likely to occur as shown in FIG. 11B.

Consequently, when the individual chip is mounted on a lead frame 5 for connecting via a wire 6, there is a high possibility that the wire 6 comes in contact with the burr 4 a, that becomes a factor of malfunction of a product.

SUMMARY OF THE INVENTION

An object of the present invention is to provide a semiconductor wafer, semiconductor chip and a dicing method of a semiconductor wafer that can prevent the generation of a burr due to the dicing, thereby enhance a yield in IC production.

A semiconductor wafer of the present invention comprising:

a plurality of chip areas in which a number of semiconductor elements are formed;

a dicing area provided at the outside of each chip area;

a characteristic evaluating element formed in the dicing area; and

a probe-contactable monitoring pad formed in the dicing area and electrically connected to the characteristic evaluating element;

wherein the monitoring pad includes two or more exposed surfaces divided via a space that is approximately parallel to the longitudinal direction of the dicing area.

A semiconductor chip of the present invention comprising:

a chip area in which a number of semiconductor elements are formed;

a dicing area provided at the outside of the chip area; and

a metal wiring formed in the dicing area;

wherein the metal wiring is not exposed on a dicing cutting surface.

A method of the present invention for dicing a semiconductor wafer having:

a plurality of chip areas in which a number of semiconductor elements are formed;

a dicing area provided at the outside of each chip area;

a characteristic evaluating element formed in the dicing area; and

a metal wiring formed in the dicing area and electrically connected to the characteristic evaluating element;

this method including a step of relatively moving a blade along a longitudinal direction of the dicing area for cutting a portion of the dicing area out,

wherein a coordinate axis Y is defined by a dicing center line, a coordinate axis X is defined by a direction perpendicular to the dicing center line, D is defined by a thickness of a cutting edge of the blade and ±σ is defined by a relative positioning error between the dicing blade and the semiconductor wafer in the direction of X and, in case where the dicing area is demarcated into five areas that are an area A (−D/2+σ<x<D/2−σ), an area B1 (−D/2−σ<x<−D/2+σ), an area B2 (D/2−σ<x<D/2+σ), an area C1 (x<−D/2−σ) and an area C2 (D/2+σ<x), the metal wiring is exposed in any one of areas of A, C1 and C2 while the metal wiring is not exposed in the areas B1 and B2.

According to the invention, in case where a characteristic evaluating element and monitoring pad are formed in a dicing area of a wafer, the monitoring pad is divided into two or more exposed surfaces, among which a space is provided that is approximately parallel to the longitudinal direction of the dicing area, whereby a blade can be positioned so as not to cross over a metal wiring. Consequently, an abruption or a burr of the metal wiring can be prevented during dicing, thereby enhancing a yield and reliability of an IC product.

BRIEF DESCRIPTION OF THE DRAWINGS

These and other objects and features of the present invention will become clear from the following description taken in conjunction with the preferred embodiments thereof and the accompanying drawings throughout which like parts are designated by like reference numerals.

FIG. 1A is a plan view showing one example of a semiconductor wafer according to the present invention, while FIG. 1B is a partial enlarged view thereof.

FIG. 2A is an enlarged view of a monitoring pad, while FIG. 2B is a cross-sectional view taken along a widthwise direction of a dicing area.

FIG. 3 is a plan view showing one embodiment of a dicing method of a semiconductor wafer according to the present invention.

FIG. 4 is a plan view showing another arrangement example of a monitoring pad.

FIGS. 5A and 5B are plan views showing another arrangement examples of a metal wiring, wherein FIG. 5A is a preferable arrangement, while FIG. 5B is an unsuitable arrangement.

FIGS. 6A and 6B are plan views showing yet another arrangement examples of a metal wiring, wherein FIG. 6A is a preferable arrangement, while FIG. 6B is an unsuitable arrangement.

FIGS. 7A and 7B are plan views showing yet another arrangement examples of a metal wiring, wherein FIG. 7A is a preferable arrangement, while FIG. 7B is an unsuitable arrangement.

FIGS. 8A and 8B are plan views showing still another arrangement examples of a metal wiring.

FIG. 9A is a plan view showing still another arrangement example of a metal wiring, while FIGS. 9B and 9C are cross-sectional views thereof.

FIG. 10 is a plan view showing another arrangement example of a monitoring pad.

FIG. 11 is an explanatory view showing one example of a conventional IC production process, wherein FIG. 11A shows a dicing process, FIG. 11B shows a state after the dicing and FIG. 11C shows a wire bonding process.

DETAILED DESCRIPTION OF THE PREFERRED EMBODIMENTS Embodiment 1

FIG. 1A is a plan view showing one example of a semiconductor wafer according to the present invention, and FIG. 1B is a partial enlarged view thereof. A wafer 10 has a substrate made of a semiconductor such as Si, GaAs or the like, on which circuit elements such as an FET (field-effect transistor), a bipolar transistor, resistor, capacitor or the like, wirings for electrically connecting these circuit elements and electrical insulating layer for insulating the wirings from one another are formed by repeatedly applying various processes such as a film-formation, mask-formation, etching, mask-removal, ion implantation or the like. Rectangular chip areas 11 where a great number of semiconductor elements are integrated are arranged in matrix in the wafer 10. Provided at the outer periphery of each chip area 11 are dicing areas 12 for cutting.

The dicing areas 12 are also referred to as “scribe areas” that are out of IC design. As shown in FIG. 1B, formed generally on each dicing area 12 is a characteristic evaluating element 20 for evaluating various manufacturing processes or characteristics of the wafer 10. The characteristic evaluating element 20 is also referred to as TEG (test element groups). Forming the characteristic evaluating element 20 by using the same process as the circuit element in the chip area 11 enables to indirectly evaluate the characteristics of the circuit element in the chip area 11.

The characteristic evaluating element 20 is made of an FET element or the like. Each terminal of the element is electrically connected to a monitoring pad 30 via a metal wiring 25. Although FIG. 1B only illustrates the metal wiring 25 and monitoring pad 30 connected to a source terminal of the FET, similar metal wiring 25 and monitoring pad 30 are provided to a gate terminal and drain terminal. Each probe of a measuring device comes in contact with each monitoring pad 30 for measuring electrical characteristics of the characteristic evaluating element 20. The metal wiring 25 and monitoring pad 30 are made of Al, Cu or alloy of these metals and arranged in the dicing area 12.

FIG. 2A shows an enlarged view of the monitoring pad 30, while FIG. 2B is a cross-sectional view taken along a widthwise direction of the dicing area 12. The monitoring pad 30 can be formed of a metal wiring of a single layer or metal wirings of plural layers. This embodiment shows an example in which the monitoring pad 30 is formed of a three-layered metal wiring.

As shown in FIG. 2B, a metal wiring 33 that is a lowermost layer, metal wirings 32 a, 32 b and 32 c that are an intermediate layer and metal wirings 31 a, 31 b and 31 c that are an uppermost layer are laminated via electrical insulating layers (not shown). According to need, through conductors 36 and 37 for causing an electrical connection in the vertical direction may be formed to penetrate the electrical insulating layer.

The metal wirings 31 a, 31 b and 31 c of the uppermost layer are exposed so as to be contactable to the probe and arranged so as to be spatially separated from one another via spaces G that are approximately parallel to the longitudinal direction of the dicing area 12. The position and size of the space G is designed considering a thickness of a cutting edge of a blade and relative positioning error. Specifically, they are designed such that the blade does not cross any metal wirings 31 a, 31 b and 31 c when the blade passes through the dicing area 12 in the dicing process.

The probe-contactable surface is divided into a plurality of exposed surfaces by providing the space G, thereby being capable of preventing an abruption or a burr of the metal wiring during the dicing process. Consequently, a yield and reliability of an IC product are enhanced.

This embodiment shows that the probe-contactable surface of the monitoring pad 30 is divided into three, but it may be divided into two or four or more exposed surfaces so long as being in the dicing area 12 and in the place other than the space G. Further, the metal wiring 25 formed by the same manner as the monitoring pad 30 is preferably arranged in the place other than the space G from the viewpoint of preventing a burr.

In case where the monitoring pad 30 is formed of metal wirings of plural layers, at least one layer among the metal wirings of the inner layer is preferably divided with the same shape as the uppermost exposed surfaces like the metal wirings 32 a, 32 b and 32 c in the intermediate layer. This can prevent an abruption or a burr of the metal wirings of the inner layer during the dicing process.

FIG. 3 is a plan view showing one embodiment of a dicing method of a semiconductor wafer according to the present invention. The dicing area 12 is provided between the adjacent chip areas 11. As shown in FIG. 2, the monitoring pad 30 has three probe-contactable surfaces including metal wirings 31 a, 31 b and 31 c, which are arranged in a place other than the space G.

The blade 9 moves relatively parallel to the longitudinal direction of the dicing area 12. The blade 9 may linearly moves while the wafer stays, or a wafer stage loaded with the wafer 12 may linearly moves while the blade 9 stays. The blade 9 for use generally has a thickness D of the cutting edge smaller than the width of the dicing area 12, so that a portion of the dicing area 12 is actually cut away. Accordingly, two cutting lines CL are formed at the positions on both sides that are far from the dicing center line of the blade 9 by a distance D/2.

Here, a coordinate axis Y is defined by the dicing center line, a coordinate axis X is defined by a direction perpendicular to the dicing center line, D is defined by the thickness D of the cutting edge of the blade and a is defined by a relative positioning error between the dicing blade and the semiconductor wafer in the direction of X, wherein the error ±σ is a total of the positioning error of the blade 9 and the positioning error of the wafer 10, which can be determined by a precision of a blade moving mechanism and a wafer stage moving mechanism.

Then, the dicing area 12 can be demarcated into five areas A, B1, B2, C1 and C2 as follows:

Area A (−D/2+σ<x<D/2−σ)

Area B1 (−D/2−σ<x<−D/2+σ)

Area B2 (D/2−σ<x<D/2+σ)

Area C1 (x<−D/2−σ)

Area C2 (D/2+σ<x)

As shown in FIG. 3, the area A includes the dicing center line and is defined by lines inward from both cutting lines CL by a distance σ. This area A is always cut away by the dicing, so that the cutting lines CL do not pass this area A even if the position of the blade 9 or the wafer 10 is deviated from −σ to +σ.

The area B1 is defined by a range from −σ to +σ centering about the lower cutting line CL. The area B2 is defined by a range from −σ to +σ centering about the upper cutting line CL. The cutting lines CL pass these areas B1 and B2 when the position of the blade 9 or the wafer 10 is deviated from −σ to +σ.

The area C1 is defined by a line outward from the lower cutting line CL by a distance σ. The area C2 is defined by a line outward from the upper cutting line CL by a distance σ. The cutting lines CL do not pass these areas C1 and C2 even if the position of the blade 9 or the wafer 10 is deviated from −σ to +σ.

Accordingly, the probe-contactable surface is divided into plural exposed surfaces such that the metal wirings 31 a, 31 b and 31 c are exposed in any one of the areas A, C1 and C2, while these wirings are not exposed in the areas B1 and B2, resulting in preventing an abruption or a burr of the metal wiring during the dicing process. Consequently, an yield and reliability of the IC product are enhanced.

Further, the spaces G existing respectively among the metal wirings 31 a, 31 b and 31 c are preferably set to have widths same as or greater than the area B1 or B2.

Thus a rectangular semiconductor chip can be obtained when the semiconductor wafer including metal wirings 31 a, 31 b and 31 c, each position and shape of which are devised, is cut by the blade 9 along the vertical and lateral directions. This semiconductor chip has a portion of the dicing areas 12 and a portion of the metal wirings remained at the outside of the chip area 11, so that the metal wirings are not exposed on the dicing cut surface. As a result, an abruption or a burr of the metal wiring due to the dicing can be prevented, thereby enhancing the yield and reliability of the IC product.

Embodiment 2

FIG. 4 is a plan view showing another arrangement example of the monitoring pad. The monitoring pad 30 can be formed of a metal wiring of a single layer or metal wirings of plural layers. The monitoring pad 30 at the left side has two probe-contactable surfaces comprising metal wirings 31 b and 31 c, which are arranged in any areas of A, C1 and C2. Specifically, the metal wirings are not arranged in the areas B1 and B2.

The monitoring pad 30 at the right side has six probe-contactable surfaces comprising metal wirings 31 a to 31 f. The metal wirings 31 a and 31 b are arranged in the area C1, the metal wirings 31 c and 31 d are arranged in the area A and the metal wirings 31 e and 31 f are arranged in the area C2. The metal wiring is not arranged in the areas B1 and B2.

These monitoring pads 30 can prevent an abruption or a burr of the metal wiring during the dicing process as mentioned above.

Embodiment 3

FIGS. 5A and 5B are plan views showing another arrangement examples of the metal wirings. FIG. 5A shows a preferable arrangement, while FIG. 5B shows an unsuitable arrangement. The monitoring pad 30 and metal wiring 25 can be formed of a metal wiring of a single layer or metal wirings of plural layers, and are electrically connected to the characteristic evaluating element 20 such as FET or the like.

The metal wirings 31 a, 31 b and 31 c are exposed so as to be contactable to the probe, and arranged in the areas A, C1 and C2. The metal wiring 25 can similarly be arranged in any areas A, C1 and C2, e.g. arranged in the area A in FIG. 5A. The metal wiring is not arranged in the areas B1 and B2 where the dicing cutting surfaces can be passed, thereby being capable of preventing an abruption or a burr of the metal wiring due to the dicing.

On the other hand, the metal wiring 25 is arranged so as to cross the areas B1 and B2 in FIG. 5B. As a result, the dicing cutting surface crosses over the metal wiring 25, thereby having possibilities of causing an abruption or a burr of the metal wiring.

Embodiment 4

FIGS. 6A and 6B are plan views showing another arrangement examples of the metal wirings. FIG. 6A shows a preferable arrangement, while FIG. 6B shows an unsuitable arrangement. The monitoring pad 30 and metal wiring 25 are electrically connected to the characteristic evaluating element 20 such as FET or the like.

the metal wirings 31 a, 31 b and 31 c are arranged in the areas A, C1 and C2. In FIG. 6A, the metal wiring 25 is arranged in the area C1 and not arranged in the areas B1 and B2 where the dicing cutting surfaces can be passed, thereby being capable of preventing an abruption or a burr of the metal wiring due to the dicing.

On the other hand, the metal wiring 25 is arranged in the areas B1 and C1 in FIG. 6B. As a result, the dicing cutting surface crosses over the metal wiring 25, thereby having possibilities of causing an abruption or a burr of the metal wiring.

Embodiment 5

FIGS. 7A and 7B are plan views showing another arrangement examples of the metal wirings. FIG. 7A shows a preferable arrangement, while FIG. 7B shows an unsuitable arrangement. The monitoring pad 30 and metal wiring 25 are electrically connected to the characteristic evaluating element 20 such as FET or the like.

The metal wirings 31 a, 31 b and 31 c are arranged in the areas A, C1 and C2. In FIG. 7A, the metal wiring 25 is arranged in the area A and not arranged in the areas B1 and B2 where the dicing cutting surfaces can be passed, thereby being capable of preventing an abruption or a burr of the metal wiring due to the dicing.

On the other hand, the metal wiring 25 is arranged in the areas A, B1 and B2 in FIG. 7B. As a result, the dicing cutting surface crosses over the metal wiring 25, thereby having possibilities of causing an abruption or a burr of the metal wiring.

Embodiment 6

FIGS. 8A and 8B are plan views showing another arrangement examples of the metal wirings. The monitoring pad 30 and metal wirings 25 and 26 can be formed of a metal wiring of a single layer or metal wirings of plural layers, and are electrically connected to the characteristic evaluating element 20 such as FET or the like.

The metal wirings 31 a, 31 b and 31 c are arranged in the areas A, C1 and C2. Two metal wirings 25 are arranged in the area C1. The metal wiring 26 that is an inner layer for electrically connecting these metal wirings 25 passes through the areas C1, B1, A, B1 and C1 in this order in FIG. 8A, while the metal wiring 26 passes through the areas C1, B1 and A in this order in FIG. 8B.

According to the above-mentioned structure, the metal wiring 26 is always cut off by dicing, causing that the monitoring pad 30 is electrically floated from the characteristic evaluating element 20. Therefore, a short-circuit can be prevented even if a bonding wire comes in contact with the monitoring pad 30.

Embodiment 7

FIG. 9A is a plan view showing another arrangement example of the metal wirings, while FIGS. 9B and 9C are cross-sectional views thereof. At the cross-point in the dicing area 12, the areas A, B1, B2, C1 and C2 relating to the dicing area in the X-direction cross over the areas A, B1, B2, C1 and C2 relating to the dicing area in the Y-direction. In particular, the overlapped area of the areas A is always cut away by dicing.

At the cross-point in FIG. 9B, the metal wiring 25 for bridging is arranged at the uppermost layer, which is electrically connected to the metal wiring 26 that is the inner layer via a through conductor for going around a metal wiring 27 that is another inner layer.

At the cross-point in FIG. 9C, a wiring 28 for bridging is arranged at the lowermost layer as well as the metal wiring 25 for bridging arranged at the uppermost layer. They are electrically connected via the metal wiring 26 that is the inner layer and the through conductor for going around the metal wiring 27 that is another inner layer. In case the wiring 28 is formed of non-metal wiring, for example, is formed of a high-resistance material such as polysilicon or the like, an electrical resistance at the bridge portion can be reduced by connecting the uppermost metal wiring 25 in parallel.

This structure assures to cut the metal wiring 25 at the uppermost layer away by dicing, thereby being capable of certainly cutting off the electrical connection between the metal wirings 26.

Embodiment 8

FIG. 10 is a plan view showing another arrangement example of the monitoring pad. The monitoring pad 30 can be formed of a metal wiring of a single layer or metal wirings of plural layers and has three probe-contactable surfaces comprising metal wirings 31 a, 31 b and 31 c, which are arranged in any one of the areas A, C1 and C2 and not arranged in the areas B1 and B2.

Further, a passivation film 40 made of an electrical insulating material is generally formed on the chip area 11 in order to protect the IC chip. The passivation film 40 partially covers the metal wirings 31 a and 31 c exposed in the areas C1 and C2.

This passivation film 40 reduces a possibility that the bonding wire comes in contact with the metal wirings 31 a and 31 c, thereby being capable of preventing a defective in short-circuit. On the other hand, the metal wirings 31 a and 31 c preferably have a wider exposed area since they function as a probe-contactable surface. Accordingly, the edge position of the passivation film 40 is determined by considering both of the wire short-circuit and exposed area. Further, the edge of the monitoring pad 30 crossing over the blade is preferably not covered with the passivation film 40 since a stress due to dicing is concentrated on the edge.

Although the present invention has been fully described in connection with the preferred embodiments thereof and the accompanying drawings, it is to be noted that various changes and modifications are apparent to those skilled in the art. Such changes and modifications are to be understood as included within the scope of the present invention as defined by the appended claims unless they depart therefrom. 

1-7. (canceled)
 8. A method of manufacturing a semiconductor device comprising steps of: preparing a semiconductor wafer having a plurality of chip areas in which a number of semiconductor elements are formed, a dicing area provided at the outside of each chip area, a characteristic evaluating element formed in the dicing area and a probe-contactable monitoring pad formed in the dicing area and electrically connected to the characteristic evaluating element, the monitoring pad including two or more exposed surfaces divided via a space that is approximately parallel to a longitudinal direction of the dicing area; and relatively moving a blade along the longitudinal direction of the dicing area for cutting a portion of the dicing area out so that a cutting line by the blade is positioned in a space between one and another of the exposed surfaces, wherein the one exposed surface is cut away and the other exposed surfaces is left.
 9. The method of claim 8, wherein the monitoring pad is formed of metal wirings of plural layers and said exposed surfaces are configured of metal wirings of the uppermost layer and at least one layer among the metal wirings of the inner layer is divided with the same shape as the exposed surface.
 10. The method of claim 8, wherein the two or more exposed surfaces are electrically connected with each other via a metal wiring of an inner layer in the semiconductor wafer before cutting by the blade.
 11. A method of manufacturing a semiconductor device comprising steps of: preparing a semiconductor wafer having a plurality of chip areas in which a number of semiconductor elements are formed, a dicing area provided at the outside of each chip area, a characteristic evaluating element formed in the dicing area and a metal wiring formed in the dicing area and electrically connected to the characteristic evaluating element; and relatively moving a blade along a longitudinal direction of the dicing area for cutting a portion of the dicing area out, wherein a coordinate axis Y is defined by a dicing center line, a coordinate axis X is defined by a direction perpendicular to the dicing center line, D is defined by a thickness of a cutting edge of the blade and ±σ is defined by a relative positioning error between the dicing blade and the semiconductor wafer in the direction of X and, in case where the dicing area is demarcated into five areas that are an area A (−D/2+σ<x<D/2−σ), an area B1 (−D/2−σ<x<−D/2+σ), an area B2 (D/2−σ<x<D/2+σ), an area C1 (x<−D/2−σ) and an area C2 (D/2+σ<x), the metal wiring is exposed in any one of areas of A, C1 and C2 while the metal wiring is not exposed in the areas B1 and B2.
 12. The method of claim 11, wherein the semiconductor wafer has a second metal wiring formed under said metal wiring in the dicing area, and the second metal wiring is formed in any one of areas of A, C1 and C2 while the second metal wiring is not formed in the areas B1 and B2.
 13. The method of claim 11, wherein the metal wirings of plural layers is formed in the dicing area and the metal wiring of the uppermost layer is arranged in any one of areas A, C1 and C2 and the metal wiring of the inner layer is arranged so as to cross any one of the areas B1 and B2. 